Analisis Fisik dan Mekanik pada Pengembangan Panel Komposit Limbah Serbuk Kayu

Siswanti Zuraida, Sastita Pratiwi

Abstract

This research discusses about comparison, testing, and analyzing composite materials for develop the building panels for lightweigh-wall applications made from wood-industrial waste materials. Wood sawdust is used as a composite cement mixture as a binder of all materials with the mixture 0%, 5%, 10%, 15%, and 20% of total weight. This research uses quantitative methods with blocks as a sample sizes 10cm x 3cm x 1cm. The test includes flexible test, porosity test, and composite walldensity test to find out mechanical and physical properties of composite material. The result of this research shows that the usage of wood sawdust as a mixture for making composite panel with 0.4 water-factor at 28 days-age get the optimum value at 15% of mixture variation with flexibility of 7.18 MPa, density 1.61 kg/m³ and compressive strength of 58.42, MPa. These results indicate that the wall panel meets the requirement of SNI 03-0349-1989 with concrete steel-brick level IV as a non-structural brick. Based on these results, it can be concluded that composite panel can be used on the wall as an effort to reduce the impact of the ruins of the building, and reduce the danger as a disaster mitigation effort.

Keywords

wood waste composite panel, recycled waste material, bending testing, compressive testing, porosity, densit

Full Text:

PDF

References

Humas BNPB. (2017). Potensi dan Ancaman Bencana. Badan Nasional Penanggulangan Bencana: https://www.bnpb.go.id

Ahmad., N.Mohamad. (2000). Struktur Behaviour of Precast Lightweight Concrete Sandwich Panel Under Eccerntic: An Overview. International Journal of Civil and Environmental Engineering.

Sumarlin, S. L. (2010). Produktivitas Material Beton Ringan dalam Pemakaian sebagai Konstruksi Dinding. Jurnal Konferensi Nasional Teknik Sipil 4.

Goritman, Birdyant., Dkk. (2011). Studi Kasus Perbandingan Berbagai Bata Ringan dari Segi Material, Biaya dan Produktifitas.

Pari, G. (2002). Industri Pengolahan Kayu Teknologi Alternatif Pemanfaatan Limbah.

Puwanto. D. (2014). Sifat Fisik Mekanik Papan Semen dari Limbah Kulit Kayu Galam. Bakri., Endra, G., dkk. (2006). Sifat Fisik dan Mekanik Komposit Kayu Semen Serbuk Gergaji.

Krisdianto, A. ( 2016). Karakteristik Komposit Serbuk Kayu Jati dengan Fraksi Volume 25%, 30%, 35% Terhadap Uji Bending, Uji Tarik dan Daya Serap Bunyi untuk Dinding Peredam Suara. Skripsi: Tenik Sipil Muhammadiyah Surakarta.

Puja, Gusti Ketuk. (2011). Study Kekuatan Tarik dan Koefisien Gesek Bahan Komposit Arang Limbah Serbuk Gergaji Kayu Jati dengan Matrik Epoxy. Jurnal Mekanika Vol 9, No. 2

Behnood, A., Verian, K., Modiri, M. (2015) Evaluation of the Splitting Tensile Strenght in Plain and Steel Fiber-Reinforced Concrete Bassed on the Compressite Strength. Construction and Building Materials 98:519-529.

Barham, Shawn; Darwin, David. (1999). Effects of Aggregate Type, Water-to- Cementitious Material Ratio, and Age on Mechanical and Fracture Properties of Concrete. Structural Engineering and Engineering Materials.

ACI 363R-92. (1997). State-of-the-Art Report on High-Strength Concrete.

Lesmana, Surya. (2018). Uji Densitas dan Porositas pada Batuan dengan Menggunakan Neraca O Houss dan Neraca Pegas.

SNI 03-3449 2002. (2002). Tata Cara Rencana Pembuatan Campuran Beton Ringan dengan Agregat Ringan.